Product Details:
|
Name: | BTO Substrate | HS Code: | 3818009000 |
---|---|---|---|
Warranty: | One Year | Full Name: | Barium Titanate Single Crystal Substrate |
Polishing: | Single Side Polished Or Double Side Polished | Hardness(Mohs): | 6-6.5 |
Thermal Expansion Coefficient (/K): | 9.4 X 10-6 | Thickness: | 0.5mm, 1.0mm |
Size: | 5x5mm,10x10mm, 15x15mm, 20x20mm | ||
High Light: | Microphones barium titanate crystal,Piezoelectric Material BTO Substrate,Kinheng barium titanate crystal |
Piezoelectric material for microphones BTO substrate single crystal substrate
Barium titanate is a piezoelectric material used in microphones and other transducers.When BTO substrates are below 18℃, the phase transformation can lead to shattering of the BTO substrates. A battery thermal box must be added to the order to keep BTO substrates above 18 degrees Celsius.
Properties:
Crystal Structure |
Tetragonal ( 4m) : 9℃ < T < 130.5 ℃ a=3.99A, c= 4.04A , |
Growth Method | Top Seeded Solution Growth |
Melting Point(℃) | 1600 |
Density(g/cm3) | 6.02 |
Dielectric Constants |
ea = 3700, ec = 135 (unclamped) ea = 2400, e c = 60 (clamped) |
Index of Refraction |
515 nm 633 nm 800 nm no 2.4921 2.4160 2.3681 ne 2.4247 2.3630 2.3235 |
Transmission Wavelength | 0.45 ~ 6.30 mm |
Electro Optic Coefficients |
rT 13 = 11.7 ?1.9 pm/V rT 33 =112 ?10 pm/V rT 42= 1920 ?180 pm/V |
Reflectivity of SPPC ( at 0 deg. cut ) |
50 - 70 % ( max. 77% ) for l = 515 nm 50 - 80 % ( max: 86.8%) for l = 633 nm |
Two-wave Mixing Coupling Constant | 10 -40 cm-1 |
Absorption Loss |
l: 515 nm 633 nm 800 nm a: 3.392cm-1 0.268cm-1 0.005cm-1 |
Advantage:
1.Excellent photorefractive properties
2.High reflectivity of self-pumped phase conjugation
Product shots:
FAQ:
1.Q: Are you a factory manufacturer?
A: Yes ,we are manufacturer with 13 years experience in the scintillator crystal industry and supplied many famous brands with good quality and service.
2.Q:Where is your main market?
A:Europe, America, Asia.
Contact Person: Ivan. wang
Tel: 18964119345